I-powder yethu yesiliva inezici zokuminyana kwenqwaba ephansi, ukuhamba kahle kukagesi, uketshezi oluhle nokumelana ne-oxidation.I-Flake silver powder iyinto efanelekile yokulinganisa i-polymer, i-conductive coatings, kanye ne-electromagnetic shielding coatings.I-coating ene-flake silver powder ine-fluidity enhle, i-anti-settlement kanye nendawo enkulu yokufafaza.
Ibanga | Izici ze-Morphology | Ukusabalalisa Usayizi Wezinhlayiyana | Ukuminyana Okubonakalayo |
Idatha ye-HR401NS | I-Spherical | D50=55nm | 0.35 g/cm3 |
Idatha ye-HR402NS | I-Spherical | D50=55nm | 1.25 g/cm3 |
Idatha ye-HR403NS | I-Spherical | I-D50=150nm | 1.35 g/cm3 |
Idatha ye-HR404NS | I-Spherical | I-D50=230nm | 1.25 g/cm3 |
Idatha ye-HR405NS | I-Spherical | I-D50=200nm | 1.55 g/cm3 |
I-HR501NS | I-Dendritic | I-D50=175nm | 1.45 g/cm3 |
I-HR502NS | I-Dendritic | I-D50=320nm | 1.37 g/cm3 |
Idatha ye-HR503NS | I-Dendritic | D50=55nm | 0.35 g/cm3 |
Idatha ye-HR504NS | I-Dendritic | D50=55nm | 0.35 g/cm3 |
I-HR505NS | I-Dendritic | D50=55nm | 0.35 g/cm3 |
I-HR601NS | I-Fibrous | Ububanzi 15nm, Ubude 2 ~ 3um | 2.15 g/cm3 |
I-HR602NS | I-Fibrous | Ububanzi 35nm Ubude 1~3um | 1.75 g/cm3 |
I-conductive silver flake powder esetshenziswa embonini ye-elekthronikhi kanye ne-microelectronics, oyinki be-conductive kanye namanye ama-conductive doped Compounds, njll.
I-Nano silver powder isetshenziselwa ikakhulukazi ukunamathisela i-sintering;I-micron silver powder isetshenziselwa ikakhulukazi inki yokuqhuba kanye ne-conductive coating.I-Sintering paste isetshenziswa kakhulu kuma-electronics, ama-capacitor, ama-inductors, ingilazi yefasitela elingemuva lezimoto;I-inki ye-conductive isetshenziswa kakhulu kumakhibhodi, ekushintsheni kolwelwesi, ezibukweni zefoni ephathekayo, njll. Ukwakheka kwe-sintering paste kanye ne-conductive inki/conductive coating ngokuyisisekelo kuyafana, okwakhiwe nge-resin, i-solvent, impushana eyisiliva nezithasiselo.Umehluko ukuthi unamathisele we-sintering uqukethe impushana yengilazi, kuyilapho uyinki eqhubayo ingenayo impusha yengilazi.I-30nm kanye ne-250nm impushana yesiliva iyona esetshenziswa kakhulu ekunamathiseleni kwe-sintering.
Impushana esiliva ingasetshenziswa futhi njenge-ejenti elwa namagciwane esetshenziswa ephepheni ehlukahlukene, epulasitiki, nasezithasiselweni zendwangu.Ingasetshenziswa ngempumelelo ekwakheni, ekuvikelweni kwezinsalela zamasiko kanye nemikhiqizo yezokwelapha.